Relaxed silicon germanium substrate with low defect density

ABSTRACT

A method of forming a strained silicon layer on a relaxed, low defect density semiconductor alloy layer such as SiGe is provided.

RELATED APPLICATIONS

This application is a continuation of U.S. patent application Ser. No. 10/228,545, filed Aug. 27, 2002, and entitled, “A Relaxed Silicon Germanium Substrate with Low Defect Density,” which is hereby incorporated by reference in its entirety.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to methods used to fabricate semiconductor devices, and more specifically to a method used to form a strained silicon layer to accommodate a channel region for a metal oxide semiconductor field effect transistor (MOSFET) devices.

2. Description of Prior Art

A promising method for improving MOSFET device performance is enhancement of carrier mobility. Both hole and electron mobility enhancement can be accomplished via the employment of surface channel, tensile strained silicon layers. Strained silicon layers used for MOSFET channel regions have been formed via epitaxial growth of silicon on relaxed silicon—germanium (SiGe) pseudo substrates. Good film quality of strained silicon layers, and of relaxed SiGe layers, are important factors for enhanced performance of strained silicon MOSFET devices, however substrate layers exhibiting high defect density, in terms of dislocations, stacking faults, twins, etc., will reduce carrier mobility.

A high quality relaxed SiGe layer, to be subsequently overlaid by a strained silicon layer, can be produced via the use of a thick SiGe buffer layer deposited on an underlying semiconductor substrate. However, there are several disadvantages to the growth of a thick SiGe buffer layer. First, a thick SiGe buffer layer at a thickness greater than a micrometer negatively impacts throughput adding unwanted processing costs. Secondly, the defect density of thick SiGe layers can be as high as 1E7 defects/cm². The use of a this SiGe buffer layer on a silicon on insulator (SOI) substrate, does allow defect densities to be decreased, however still in the unacceptable range of about 1E6 defects/cm².

This invention will feature a method of obtaining a desired, strained silicon layer on a relaxed, low defect density semiconductor alloy layer, and an alloy layer such as a SiGe layer. This is accomplished via the growth of the strained silicon layer on an underlying composite layer, which in turn is comprised of a silicon layer sandwiched between two strained layers, such as SiGe layers. As the thickness of the top SiGe strained layer of the composite layer increases via epitaxial growth, dislocations form in the sandwiched, initially unstrained silicon layer, allowing the top, or overlying initially strained alloy layer to relax, and exhibit a low defect density. The desired strained silicon layer is now epitaxially grown on the underlying, relaxed semiconductor alloy layer. A key advantage of this invention is the low dislocation density in the relaxed SiGe layer, underlying the strained silicon layer. Prior art such as Chu, et al., in U.S. Pat. No. 6,059,895, as well as Ek, et al., in U.S. Pat. No. 5,759,898, describe methods of forming tensile strained silicon layers via SiGe relaxed layers, however these prior arts do not describe the novel process sequence disclosed in this present invention in which a strained silicon layer is formed on a relaxed, low defect density, semiconductor alloy layer.

SUMMARY OF THE INVENTION

It is an object of this invention to form a strained silicon layer, for use as a channel region for a MOSFET device.

It is another object of this invention for form a composite layer comprised of a silicon layer, sandwiched between strained SiGe layers, and with increasing growth of the top SiGe layer create defects in the underlying silicon layer, while converting the overlying, strained SiGe layer to a relaxed, low defect density SiGe layer.

It is another object of this invention to grow a strained silicon layer on the underlying composite layer, with the strained silicon layer grown on the relaxed, low defect density SiGe layer.

In accordance with the present invention a method of forming a strained silicon layer on a relaxed, low defect density semiconductor alloy layer, for use as a channel region for a MOSFET device is described. After growth of an underlying strained layer, such as silicon—germanium (SiGe) layer, on a semiconductor or on an SOI substrate, an unstrained silicon layer is epitaxially grown, followed by epitaxial growth of an overlying strained layer, such as a SiGe layer. As the thickness of overlying, strained SiGe layer increases strain is induced in the underlying silicon layer via dislocation formation, resulting in a strained silicon layer, while relaxing the strain, and lowering the defect density of the overlying SiGe layer. A strained silicon layer is then epitaxially grown on the underlying, relaxed low defect density SiGe layer.

BRIEF DESCRIPTION OF THE DRAWINGS

The object and other advantages of this invention are best described in the preferred embodiment with reference to the attached drawings that include:

FIGS. 1-5, which schematically, in cross-sectional style, describe key stages of fabrication for obtaining a strained silicon layer on an underlying composite layer, wherein the overlying component of the composite layer is a relaxed, low defect density semiconductor alloy layer.

FIGS. 6-7, which schematically, in cross-sectional style, describe key stages in fabrication for a second embodiment of this invention, in which a strained silicon layer is formed on a relaxed, low defect density semiconductor alloy layer, wherein the semiconductor alloy layer was subjected to an anneal procedure performed either during or after the epitaxial growth to reduce the defect density of the annealed semiconductor alloy layer.

FIGS. 8-9, which schematically, in cross-sectional style, describe key stages of fabrication for a third embodiment of this invention, in which a silicon layer is subjected to ion implantation procedures to allow an overlying SiGe layer to be epitaxially grown, and now feature a defect density lower than defect densities of counterpart SiGe layers epitaxially grown on non-implanted silicon.

FIG. 10, which schematically, in cross-sectional style, describes a MOSFET device formed featuring a strained silicon layer.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

A method of forming a strained silicon layer on a relaxed, low defect density semiconductor alloy layer, such as SiGe, silicon layer, will now be described in detail. Substrate 1, schematically shown in FIG. 1, can be a semiconductor substrate such as a single crystalline, silicon substrate, or substrate 1, can be silicon on insulator (SOI) substrate. Strained layer 2, a semiconductor alloy layer such as SiGe, is epitaxially grown on substrate 1, via chemical vapor deposition (CVD), or via molecular beam epitaxy, to a thickness below the critical thickness. Strained layer 2, is epitaxially grown using silane, or disilane as a silicon source, while germane is used as the germanium source. Strained layer 2, is kept thin, less than the critical thickness, so that relaxation of this layer does not occur. Strained layer 2, is formed with a natural lattice constant different than the lattice constant of semiconductor substrate 1.

Silicon layer 3, is next epitaxially grown on strained layer 2, to a thickness less than 500 Angstroms. Silicon layer 3, schematically shown in FIG. 2, is epitaxially grown using silane or disilane as a source. Silicon layer 3, is grown with a natural lattice constant different than the natural lattice constant of strained layer 2.

Growth of another semiconductor layer is next addressed, attempting to obtain a relaxed, low defect density layer. A first stage of obtaining a relaxed, low defect density layer initiates with a first stage of an epitaxial growth procedures, resulting in the epitaxial growth of thin strained layer 4 a, wherein the thin strained layer is a semiconductor layer 4 a, such as SiGe layer, and wherein the content of germanium in semiconductor layer 4 a, is between about 5 to 80 weight percent. Thin, strained layer 4 a, is again obtained via molecular beam epitaxy or via chemical vapor deposition featuring metal organic CVD procedures using silane, or disilane as a source for silicon, while germane is used as a source for germanium. This is schematically shown in FIG. 3. As the thickness of the overlying strained layer increases during a second stage of the epitaxial growth procedure, strain is induced in the underlying, initially unstrained silicon layer 3. When the strain in silicon layer 3, causes its critical thickness to decrease between its physical thicknesses, dislocations in silicon layer 3, will ensue converting initially unstrained silicon layer 3, to a strained silicon layer. In addition, and of utmost importance, the dislocation formation in strained silicon layer 3, results in relaxation of overlying strained layer 4 a, resulting in a relaxed SiGe layer 4 b, now at a final thickness between about 4000 Angstroms to several um. The natural lattice constant of SiGe layer 4 b, is different than the natural lattice constant of underlying silicon layer 3. The result of the epitaxial grown is schematically shown in FIG. 4. Thus, the desired feature of forming a relaxed, low density layer, such as relaxed, low density semiconductor alloy layer 4 b, is achieved, with this relaxed SiGe layer 4 b, now providing a defect density of less than 1E3 defects/cm². The low defect density of layer 4 b, which will subsequently be located underlying a strained silicon layer, will minimize the leakage path for subsequent MOSFET devices formed in a subsequently overlying strained silicon layer.

Critical, silicon layer 10, the desired layer to be used to accommodate the channel region for subsequent CMOS devices, is next epitaxially grown, and schematically shown in FIG. 5. Silicon layer 10, is epitaxially grown using silane or disilane as a source. The thickness of silicon layer 10, is less than its critical thickness to maintain the desired strain in silicon layer 10. Thus, the desired configuration needed to accommodate high performance, low leakage MOSFET devices, a strained silicon layer, on an underlying, relaxed low defect density layer, has been achieved via use of the above first embodiment of the invention.

A second embodiment of this invention, the process of forming a strained silicon layer on a relaxed, low defect density semiconductor layer, is next addressed and schematically shown using FIGS. 6-7. Epitaxial growth of the identical composite layer described in the previous embodiment via growth conditions, and using thickness identical to those used and previously described for the first embodiment of this invention, is again performed, however, for this case followed by an anneal procedure. The anneal procedure results in additional relaxation of the overlying, SiGe layer, as well as additional decreases in defect density of this layer, when compared to counterpart SiGe layers not subjected to the anneal procedure. Anneal procedure 5, can be performed to thin, strained SiGe layer 4 a, at a stage prior to completing the entire epitaxial growth procedure, then followed by additional epitaxial growth resulting in relaxed, low defect density, SiGe layer 4 b, as shown schematically in FIG. 6. If desired, the anneal procedure can also be performed after the entire layer of the relaxed, low defect density layer has been realized. For either case, the anneal procedure is performed in an inert ambient, at a temperature between 800 to 1200° C., resulting in a final thickness for SiGe layer 4 b, again-between about 4000 Angstrom to several um. Critical, silicon layer 10, again the desired layer to be used to accommodate the channel region for subsequent CMOS devices, is next epitaxially grown, and schematically shown in FIG. 7. Silicon layer 10, is epitaxially grown using silane or disilane as a source. The thickness of silicon layer 10, is grown to a value less than its critical thickness to maintain the desired strain in silicon layer 10. The ability to epitaxially grow strained silicon layer 10, with enhanced tensile strain, is enhanced via the additional relaxation and decreased defect density of annealed SiGe. This is schematically shown in FIG. 7.

A third embodiment of this invention entails the use of ion implantation procedure 7, to weaken silicon layer 3, to allow overlying semiconductor alloy layer 4 b, to be epitaxially grown again with increased relaxation and decreased defect density, when compared to counterpart layers formed on non-implanted, underlying silicon layers. The ability to obtain a relaxed, low defect density SiGe layer, improves the ability to subsequently grow a thin, strained silicon layer, under tensile strain. Growth of SiGe layer 4 b, shown schematically in FIG. 8 featuring enhanced relaxation and low defect density, less than 1E3 defects/cm², as a result of epitaxial growth on an underlying, implanted silicon layer, is next accomplished at an identical thickness, as well as using identical process parameters, as used with counterpart SiGe layers described in the previous embodiments. The attainment of SiGe layer 4 b, featuring the improved parameters, again allows the epitaxial growth of strained silicon layer 10, to be accomplished, wherein the critical thickness of strained silicon layer 10, is minimized to maintain strain, and to avoid relaxation. This is schematically shown in FIG. 9. If desired ion implantation procedure 7, can be applied to silicon layer 3, at some point after growth of an initial portion of strained layer 4 b. This would be accomplished using an energy higher than the energy used for implantation prior to any growth of strained layer 4 b.

The formation of a MOSFET device, with a channel region located in strained silicon layer 10, and with the leakage characteristics of the MOSFET device improved via formation on relaxed, low defect density, SiGe layer 4 b, is next described and schematically shown in FIG. 10. Gate insulator layer 11, comprised of silicon dioxide is thermally grown in an oxygen—stream ambient. A conductive layer, such as doped polysilicon or metal is deposited on gate insulator layer 11. Photolithographic and dry etching procedures are next employed to define conductive gate structure 12. If desired, lightly doped source/drain region 13, is formed in regions of silicon layer 10, not covered by conductive gate structure 12. Lightly doped source/drain region 13, is obtained via ion implantation procedures, using either N type ions if an N channel MOSFET is desired, or using P type ions is a P channel MOSFET device is needed. Insulator spacers 14, such as silicon oxide or silicon nitride spacers, are formed on the sides of conductive gate structure 12, via deposition of the insulator layer followed by a blanket anisotropic dry etch procedure. Finally, heavily doped source/drain region 15, obtained via implantation of either N type, or P type ions, is formed in a region of strained silicon layer 10, not covered by conductive gate structure 12, or by insulator spacers 14.

Although this invention has been described using a Si/SiGe combination, similar results can be obtained using a SiGe/SiGeC system, in which SiGe is an initially unstrained layer, converted to a strained layer via dislocation formation induced via growth of an overlying strained SiGeC layer, with the overlying SiGeC layer relaxing, and featuring a low defect density, after conversion the underlying SiGe layer. Other combination of materials offering the ability to create strained channel regions include elemental, alloy, and compound semiconductors, (such as InGaAs/GaAs, AlGaAs/GaAs, and InGaN/GaN).

While this invention has been particularly shown and described with reference to, the preferred embodiments thereof, it will be understood by those skilled in the art that various changes in form and details may be made without departing from the spirit and scope of this invention. 

1. A method of fabricating several crystalline layers on a crystalline substrate, comprising the steps of: growing a first crystalline layer of a first natural crystal lattice constant that is different from the lattice constant of said crystalline substrate, on said crystalline substrate; growing a second crystalline layer of a second natural constant that is different from the natural constant of said first crystalline layer, on said first crystalline layer; and growing a third low defect density crystalline layer of a third natural constant that is different from the natural constant of said second crystalline layer, on said second crystalline layer, as to promote the creation of defects into at least said second crystalline layer, wherein the grown of an initial portion of said third low defect density crystalline layer results in a strained layer however becoming a relaxed layer during the growth of a final portion of said third low defect density crystalline layer, with the relaxation of said third low defect density crystalline layer resulting in defects and dislocations induced in said underlying, second crystalline layer.
 2. The method of claim 1, further including growth of a strained thin fourth crystalline layer on said third low defect density crystalline layer of claim 1, wherein the natural lattice constant of said fourth crystalline layer is different from the natural lattice constant of said third low defect density crystalline layer.
 3. The method of claim 2, wherein said fourth crystalline layer is a compound semiconductor.
 4. The method of claim 2, wherein said fourth crystalline layer is a semiconductor alloy.
 5. The method of claim 2, wherein said fourth crystalline layer is silicon.
 6. The method of claim 2, wherein MOSFETs are fabricated at least partially in a strained fourth crystalline layer.
 7. The method of claim 1, further comprising multiple pairs of said first crystalline layer, and said second crystalline layer, on said crystalline substrate.
 8. The method of claim 1, wherein the defect density of said third low defect density crystalline layer of less than 1E6 defects/cm².
 9. The method of claim 1, wherein said crystalline substrate is a compound semiconductor.
 10. The method of claim 1, wherein said first crystalline layer is a compound semiconductor.
 11. The method of claim 1, wherein said second crystalline layer is a compound semiconductor.
 12. The method of claim 1, wherein said third low defect density crystalline layer is a compound semiconductor.
 13. The method of claim 1, wherein said crystalline substrate is a semiconductor alloy.
 14. The method of claim 1, wherein said first crystalline layer is a semiconductor alloy.
 15. The method of claim 1, wherein said second crystalline layer is a semiconductor alloy.
 16. The method of claim 1, wherein said third low defect density crystalline layer is a semiconductor alloy.
 17. The method of claim 1, wherein said crystalline substrate is silicon.
 18. The method of claim 1, wherein said first crystalline layer is a semiconductor alloy comprising of Si and Ge.
 19. The method of claim 1, wherein said second crystalline layer is silicon.
 20. The method of claim 1, wherein said third low defect density crystalline layer is a semiconductor alloy comprising of Si and Ge.
 21. The method of claim 1, wherein the defect density of said third low defect density crystalline layer is less than 1E3 defects/cm².
 22. The method of claim 1, wherein said first crystalline layer is a strained SiGe layer, obtained via epitaxial growth procedures such as molecular beam epitaxy or CVD epitaxy.
 23. The method of claim 1, wherein said third crystalline layer is a third low defect density crystalline layer comprised of SiGe, obtained via epitaxial growth procedures such as molecular beam epitaxy or CVD epitaxy.
 24. The method of claim 1, wherein the said first crystalline layer, a strained SiGe layer, is grown to a thickness below the critical thickness.
 25. The method of claim 1, wherein implantation into said first silicon crystalline layer, or into said second crystalline layer, is employed to promote generation of defects and relaxation of said third crystalline layer.
 26. The method of claim 1, wherein an anneal procedure is performed after the growth of said third crystalline layer, a low defect density SiGe layer.
 27. A structure comprising: a crystalline substrate; a first crystalline layer of first lattice constant on said crystalline substrate; a second crystalline layer on said first crystalline layer, comprised with a second lattice constant different from the first lattice constant; a third crystalline layer on said second crystalline layer, comprised with a third lattice constant different than said second lattice constant; a strained fourth crystalline layer; and a MOSFET device located at least partially in said fourth crystalline layer. 